Rust Oleum CombiColor Matt Metal Paint

RUST-OLEUM CombiColor Metal 7300/7400 coating is primer and topcoat in one, based on a urethane modified alkyd, providing good drying properties at low temperatures.
The product contains rust-inhibitive pigments and is lead- and chromate free.

Recommended Uses
Should be applied on bare, manually derusted or with CombiPrimer Anti-Corrosion 3369/3380 primed steel. CombiColor Metal is intended for brush and roller application and can also be applied by air spray.
Offers corrosion protection in a light industrial environment.
For metal structures in a more aggressive industrial environment, prior application of a RUSTOLEUM CombiPrimer Anti-Corrosion 3369/3380 is recommended.

Specifications
• Appearance: High gloss, Satin (black and white), Flat (black and white)
• Satin and High gloss are also available as tint base
• Density: High gloss/flat: 1.07kg/l. ± 0.09 depending on colour
• Satin: 1,22kg/l. ± 0,10 depending on colour
• Solids Content: High gloss/flat: 54.6% by volume ± 2.0 depending on colour
• Satin: 50,6 volume % ± 2,0 depending on colour
• Viscosity: High gloss/flat: 100 - 104 KU / Krebs Stormer Units at 20°C
• Satin: 86 - 91 KU /Krebs Stormer Units bij 20°C
• Recommended film thickness: 55 ìm dry, equals 100 ìm wet
• VOC-content: 439g/l max.
• Ready-to-use mixture: 495g/l max.
• Category: A/i
• EU Limit values: 600g/l (2007) / 500g/l (2010)

Drying times
• 20°C/50% r.h. - To touch: 2 hours / To handle: 8 hours / To recoat: After 16 hours / Full hardness: 7 days
• 10°C/60% r.h. - To touch: 3 hours / To handle: 16 hours / To recoat: After 24 hours / Full hardness: 14 days
• 30°C/50% r.h. - To touch: 1 ½ hours / To handle: 6 hours / To recoat: After 8 hours / Full hardness: 5 days
• Heat resistance: 90°C (dry heat), at elevated temperatures discoloration may occur

Coverage
Theoretical: 10.3m²/l at 55 ìm dry, depending on colour.
Practical: Practical coverage depends on many factors such as porosity and roughness of the substrate and material losses during application.